Interactions between a bismuth type leadless glaze and a bone China body during glost firing

A Kara, R Stevens

Research output: Contribution to journalArticle

Abstract

In the present study, the interactions between a high bismuth type commercial transparent leadless glaze and a biscuit fired bone china body during glost firing at different temperatures were investigated using SEM. The formation of several phases with different morphological and chemical characteristics was clearly demonstrated. It was found that the interface characteristics were similar to those previously observed at an ABS type commercial transparent leadless glaze-bone china interfaces.
Original languageEnglish
Pages (from-to)1637-1640
Number of pages4
JournalAdvances in Composite Materials and Structures, Parts 1 and 2
Volume264-268
Publication statusPublished - 2004

Fingerprint

Glazes
Bismuth
Bone
Scanning electron microscopy
Temperature

Cite this

Interactions between a bismuth type leadless glaze and a bone China body during glost firing. / Kara, A; Stevens, R.

In: Advances in Composite Materials and Structures, Parts 1 and 2, Vol. 264-268, 2004, p. 1637-1640.

Research output: Contribution to journalArticle

@article{5c633cc782424b289ca2bb6967ff734b,
title = "Interactions between a bismuth type leadless glaze and a bone China body during glost firing",
abstract = "In the present study, the interactions between a high bismuth type commercial transparent leadless glaze and a biscuit fired bone china body during glost firing at different temperatures were investigated using SEM. The formation of several phases with different morphological and chemical characteristics was clearly demonstrated. It was found that the interface characteristics were similar to those previously observed at an ABS type commercial transparent leadless glaze-bone china interfaces.",
author = "A Kara and R Stevens",
year = "2004",
language = "English",
volume = "264-268",
pages = "1637--1640",
journal = "Advances in Composite Materials and Structures, Parts 1 and 2",
issn = "1013-9826",
publisher = "Trans Tech Publications",

}

TY - JOUR

T1 - Interactions between a bismuth type leadless glaze and a bone China body during glost firing

AU - Kara, A

AU - Stevens, R

PY - 2004

Y1 - 2004

N2 - In the present study, the interactions between a high bismuth type commercial transparent leadless glaze and a biscuit fired bone china body during glost firing at different temperatures were investigated using SEM. The formation of several phases with different morphological and chemical characteristics was clearly demonstrated. It was found that the interface characteristics were similar to those previously observed at an ABS type commercial transparent leadless glaze-bone china interfaces.

AB - In the present study, the interactions between a high bismuth type commercial transparent leadless glaze and a biscuit fired bone china body during glost firing at different temperatures were investigated using SEM. The formation of several phases with different morphological and chemical characteristics was clearly demonstrated. It was found that the interface characteristics were similar to those previously observed at an ABS type commercial transparent leadless glaze-bone china interfaces.

M3 - Article

VL - 264-268

SP - 1637

EP - 1640

JO - Advances in Composite Materials and Structures, Parts 1 and 2

JF - Advances in Composite Materials and Structures, Parts 1 and 2

SN - 1013-9826

ER -