Data sets for article entitled "Structure of semiconducting versus fast-ion conducting glasses in the Ag-Ge-Se system"

Dataset

Description

Data sets used to prepare Figures 2, 4 – 13 and 15 in the article entitled “Structure of semiconducting versus fast-ion conducting glasses in the Ag-Ge-Se system” that will appear in Royal Society Open Science. The files are labelled according to the figure numbers. The data sets were created using the methodology described in the manuscript. Each of the plots was created using Origin software (http://www.originlab.com/). The data set corresponding to a plotted curve within an Origin file can be identified by clicking on that curve. The units for each axis are given on the plots.

The data sets correspond to measurements made on glassy samples along the Agx(Ge0.25Se0.75)(1-x) tie line for x in the range from 0 to 25. Figure 2 gives the mass density, figure 4 gives the glass transition temperature, figures 5 – 6 give measured neutron and x-ray diffraction data sets, figures 7 – 13 show additional neutron diffraction data sets and an analysis of those data sets, and figure 15 shows the results for a model on the composition dependence of the coordination number for Se-Se homopolar bonds.
Date made available17 Jan 2018
PublisherUniversity of Bath
Date of data production21 Sep 2008 - 15 Sep 2017

Cite this

Salmon, P. (Creator), Zeidler, A. (Creator). (17 Jan 2018): Data sets for article entitled "Structure of semiconducting versus fast-ion conducting glasses in the Ag-Ge-Se system", University of Bath. 10.15125/BATH-00423